Epitaxial Growth of Strontium Bismuth Tantalate/Niobate on Buffered Magnesium Oxide Substrates
2005
Epitaxial films of strontium bismuth tantalate (SrBi{sub 2}Ta{sub 2}O{sub 9}, SBT) and strontium bismuth niobate (SrBi{sub 2}Nb{sub 2}O{sub 9}, SBN) were grown using solution deposition techniques on magnesium oxide (MgO) substrates buffered with a 100 nm layer of lanthanum manganate (LaMnO{sub 3}, LMO). Film structure and texture analyses were carried out using x-ray diffraction. Theta-2theta diffraction patterns were consistent with a c-axis aligned structure for both the buffer layer and the solution deposited films. Theta-2 theta scans revealed (001){sub SBT, SBN}//(001) LMO epitaxial relationships between the solution deposited films and the buffer layer. A pole figure about the SBT, SBN (115) reflection indicated a single in-plane epitaxy. Film quality was assessed using {omega} and {phi} scans. Nuclear Magnetic Resonance ({sup 13}C) was used to characterized the methoxy-ethoxide solutions used for the deposition of the SBN and SBT films.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
9
References
1
Citations
NaN
KQI