Mechanical properties and thermal stability of TiN∕TiB2 nanolayered thin films

2005 
This article describes a study of TiN∕TiB2 nanolayered coatings on sapphire and M2 tool steel substrates. Residual stress in as-deposited TiN∕TiB2 varied from tensile to compressive with increasing substrate bias. Increasing the density of nanolayer interfaces (i.e., decreasing bi-layer period) decreased the compressive stress; this effect was explained by diffusion of point defects to interfaces and/or an indirect effect of interfaces on stress via film structure. A thin TiN buffer layer substantially reduced the stress and improved adhesion on steel. Nanolayer film adhesion on steel was generally intermediate between that of monolithic TiN coatings, which was good, and TiB2 coatings, which was poor. As-deposited nanolayers showed no hardness enhancement relative to rule of mixtures. X-ray diffraction results showed that the boride layers tended to be amorphous, especially for small layer thicknesses. After annealing at 1000°C, nanolayer structure was retained, thin boride layers were at least partially ...
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    45
    References
    29
    Citations
    NaN
    KQI
    []