BIOLOGY OF ALKALI-AND HEAT-TREATED TITANIUM IMPLANTS

In cementless fixation system, surface character becomes important factor. Alkali and heat treatments on titanium metal has been proved to show strong bonding to bone and higher ongrowth rate. In this study we examined the effect of alkali and heat treatments on titanium rod in rabbit femur intramedurally model, in consideration of cementless hip stem. The implant had a 5mm in diameter and 25 mm in length. The implants were and half of them were immersed in 5 mol/L sodium hydroxide solution and heated at 600 ae for one hour (AH implant), and the other half were untreated (CL implant). The implants were implanted into the distal femur of the rabbits, AH implant into left femur and CL implants into right. The bone-implant interfaces were evaluated at 3, 6, and 12 weeks after implantations.Pull-out tests showed that AH implants significantly higher bonding strength to bone than CL implants at each week after operations. At 12 weeks mean pull-out load of AH implants was 411.7 N and that of CL implants 72.2 N....