Lanthanum titanium perovskite compound: Thin film deposition and high frequency dielectric characterization

Abstract Perovskite lanthanum titanium oxide thin films were deposited on (001) MgO, (001) LaAlO 3 and Pt(111)/TiO 2 /SiO 2 /(001)Si substrates by RF magnetron sputtering, using a La 2 Ti 2 O 7 homemade target sputtered under oxygen reactive plasma. The films deposited at 800 °C display a crystalline growth different than those reported on monoclinic ferroelectric La 2 Ti 2 O 7 films. X-ray photoelectron spectroscopy analysis shows the presence of titanium as Ti 4 + ions, with no trace of Ti 3 + , and provides a La/Ti ratio of 1.02. The depositions being performed from a La 2 Ti 2 O 7 target under oxygen rich plasma, the same composition (La 2 Ti 2 O 7 ) is proposed for the deposited films, with an unusual orthorhombic cell and Cmc2 1 space group. The films have a textured growth on MgO and Pt/Si substrates, and are epitaxially grown on LaAlO 3 substrate. The dielectric characterization displays stable values of the dielectric constant and of the losses in the frequency range [0.1–20] GHz. No variation of the dielectric constant has been observed when a DC electric field up to 250 kV/cm was applied, which does not match a classical ferroelectric behavior at high frequencies and room temperature for the proposed La 2 Ti 2 O 7 orthorhombic phase. At 10 GHz and room temperature, the dielectric constant of the obtained La 2 Ti 2 O 7 films is e ~ 60 and the losses are low (tanδ