Selective etching characteristics of the AgInSbTe phase-change film in laser thermal lithography

In the current work, the etching selectivity of the AgInSbTe phase-change film in laser thermal lithography is reported for the first time. Film phase change induced by laser irradiation and etching selectivity to crystalline and amorphous states in different etchants, including hydrochloric acid, sulfuric acid, phosphoric acid, nitric acid, sodium hydroxide, sodium sulfide, ammonium sulfide and ammonium hydroxide, are investigated. The results indicated that ammonium sulfide solvent (2.5 mol/L) had excellent etching selectivity to crystalline and amorphous states of the AgInSbTe film, and the etching characteristics were strongly influenced by the laser power density and laser irradiation time. The etching rate of the crystalline state of the AgInSbTe film was 40.4 nm/min, 20 times higher than that of the amorphous state under optimized irradiation conditions (power density: 6.63 mW/μm2 and irradiation time: 330 ns), with ammonium sulfide solvent (2.5 mol/L) as etchant. The step profile produced in the selective etching was clear, and smooth surfaces remained both on the step-up and step-down with a roughness of less than 4 nm (10×10 μm). The excellent performance of the AgInSbTe phase-change film in selective etching is significant for fabrication of nanostructures with super-resolution in laser thermal lithography.