Evolution of precipitate in nickel-base alloy 718 irradiated with argon ions at elevated temperature

Abstract Alloy 718 is a nickel-base superalloy whose strength derives from γ′(Ni 3 (Al,Ti)) and γ″(Ni 3 Nb) precipitates. The evolution of the precipitates in alloy 718 irradiated with argon ions at elevated temperature were examined via transmission electron microscopy. Selected-area electron diffraction indicated superlattice spots disappeared after argon ion irradiation, which showing that the ordered structure of the γ′ and γ″ precipitates became disordered. The size of the precipitates became smaller with the irradiation dose increasing at 290 °C.