Glycerol Valorization over ZrO2-Supported Copper Nanoparticles Catalysts Prepared by Chemical Reduction Method

Copper nanoparticles (NPs) and ZrO2-supported copper NPs (Cu NPs/ZrO2) were synthesized via a chemical reduction method applying different pH (4, 7 and 9) and evaluated in a glycerol dehydration reaction. Copper NPs were characterized with transmission electron microscopy (TEM) and UV–vis spectroscopy. Transmission electron microcopy (TEM) results revealed a homogeneous distribution of copper NPs. A hypsochromic shift was identified with UV–vis spectroscopy as the pH of the synthesis increased from pH = 4 to pH = 9. Zirconia-supported copper NPs catalysts were characterized using N2 physisorption, X-ray diffraction (XRD), TEM, X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction (TPR), temperature-programmed desorption of ammonia (NH3-TPD) and N2O chemisorption. The presence of ZrO2 in the chemical reduction method confirmed the dispersion of the copper nanoparticles. X-ray diffraction indicated only the presence of tetragonal zirconia patterns in the catalysts. XPS identified the Cu/Zr surface atomic ratio of the catalysts. TPR patterns showed two main peaks for the Cu NPS/ZrO2 pH = 9 catalyst; the first peak between 125 and 180 °C (region I) was ascribed to more dispersed copper species, and the second one between 180 and 250 °C (region II) was assigned to bulk CuO. The catalysts prepared at pH = 4 and pH = 7 only revealed reduction at lower temperatures (region I). Copper dispersion was determined by N2O chemisorption. With NH3-TPD it was found that Cu NPs/ZrO2 pH = 9 exhibited the highest total quantity of acidic sites and the highest apparent kinetic constant, with a value of 0.004 min−1. The different pH applied to the synthesis media of the copper nanoparticles determined the resultant copper dispersion on the ZrO2 support, providing active domains for glycerol conversion.