Mechanical properties as an indicator of interstitials in niobium for superconducting accelerator cavities
2015
A preliminary investigation was conducted into the feasibility of using simple mechanical properties experiments to evaluate interstitial impurity uptake from processing environments. Two types of tests were examined: tensile tests and complex modulus measurements using a dynamic mechanical analyzer (DMA). For the tensile tests, samples were cut from a single crystal of niobium, with the same orientation, and then prepared following different procedures. Significant differences were observed during tensile tests, with yielding strength and strain-to-failure clearly related to interstitial uptake. When the strain rate was reduced by an order of magnitude, the strain-to-failure was reduced by 18 % indicating that interstitial hydrogen is responsible for this behavior. For the complex modulus measurement, polycrystalline samples from different locations of two different ingots were examined at a frequency of 1.0 Hz while the temperature was increased at the rate of 1.0 °C per minute. Anaelastic peaks were fo...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
26
References
1
Citations
NaN
KQI