Low temperature surface passivation for silicon solar cells
1996
Abstract Surface passivation at low processing temperatures becomes an important topic for cheap solar cell processing. In this study, we first give a broad overview of the state of the art in this field. Subsequently, the results of a series of mutually related experiments are given about surface passivation with direct Plasma Enhanced Chemical Vapour Deposition (PECVD) of silicon oxide (Si-oxide) and silicon nitride (Si-nitride). Results of harmonically modulated microwave reflection experiments are combined with Capacitance-Voltage measurements on Metal-Insulator-Silicon structures (CV-MIS), accelerated degradation tests and with Secondary Ion Mass Spectrometry (SIMS) and Elastic Recoil Detection (ERD) measurements of hydrogen and deuterium concentrations in the passivating layers. A large positive fixed charge density at the interface is very important for the achieved low surface recombination velocities S . The density of interface states D it is strongly reduced by post deposition anneals. The lowest values of S are obtained with PECVD of Si-nitride. The surface passivation obtained with Si-nitride is stable under typical operating conditions for solar cells. By using deuterium as a tracer it is shown that hydrogen in the ambient of the post deposition anneal does not play a role in the passivation by Si-nitride. Finally, the results of CV-MIS measurements (Capacitance-Voltage measurements on Metal-Insulator-Silicon structures) on deposited Si-nitride layers are used to calculate effective recombination velocities as a function of the injection level at the surface, using a model that is able to predict the surface recombination velocity S at thermally oxidized silicon surfaces. These results are not in agreement with the measured increase of S at low injection levels.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
47
References
135
Citations
NaN
KQI