Evolution of microstructure and hardness in Hf25Nb25Ti25Zr25 high-entropy alloy during high-pressure torsion

Abstract A four-component equimolar high-entropy alloy (HEA) with the composition of HfNbTiZr and body-centered cubic (bcc) structure was processed by HPT at RT. The evolution of the dislocation density, the grain size and the hardness was monitored along the HPT-processed disk radius for different numbers of turns between ¼ and 20. It was found that most of the increase of the dislocation density and the refinement of the grain structure occurred up to the shear strain of ∼40. Between the strains of ∼40 and ∼700, only a slight grain size reduction was observed. The saturated dislocation density and grain size were ∼2.1 × 10 16  m −2 and ∼30 nm, respectively. The saturation in hardness was obtained at ∼4450 MPa. These values were similar to the parameters determined in the literature for five-component HEAs processed by HPT. The analysis confirmed that the main component in the strength was given by the friction stress in the HPT-processed bcc HfNbTiZr HEA. It was also revealed that the contribution of the high dislocation density to the strength was significantly higher than the effect of the small grain size.