Results for aliovalent doping of CeBr{sub 3} with Ca{sup 2+}

Despite the outstanding scintillation performance characteristics of cerium tribromide (CeBr{sub 3}) and cerium-activated lanthanum tribromide, their commercial availability and application are limited due to the difficulties of growing large, crack-free single crystals from these fragile materials. This investigation employed aliovalent doping to increase crystal strength while maintaining the optical properties of the crystal. One divalent dopant (Ca{sup 2+}) was used as a dopant to strengthen CeBr{sub 3} without negatively impacting scintillation performance. Ingots containing nominal concentrations of 1.9% of the Ca{sup 2+} dopant were grown, i.e., 1.9% of the CeBr{sub 3} molecules were replaced by CaBr{sub 2} molecules, to match our target replacement of 1 out of 54 cerium atoms be replaced by a calcium atom. Precisely the mixture was composed of 2.26 g of CaBr{sub 2} added to 222.14 g of CeBr{sub 3}. Preliminary scintillation measurements are presented for this aliovalently doped scintillator. Ca{sup 2+}-doped CeBr{sub 3} exhibited little or no change in the peak fluorescence emission for 371 nm optical excitation for CeBr{sub 3}. The structural, electronic, and optical properties of CeBr{sub 3} crystals were studied using the density functional theory within the generalized gradient approximation. Calculated lattice parameters are in agreement with the experimental data. The energy bandmore » structures and density of states were obtained. The optical properties of CeBr{sub 3}, including the dielectric function, were calculated.« less