Developing novel Ca-zeolite/poly(amino acid) composites with hemostatic activity for bone substitute applications

AbstractThe novel Ca-zeolite/poly(amino acid) (CaY/PAA) composites for bone substitute applications with hemostatic activity were prepared using the in situ melting polymerization method. In this study, Ca-zeolite (CaY) loaded with Ca2+ was obtained from Y-type zeolite (NaY) by ion-exchange method. The properties of the CaY/PAA composites and PAA, including composition, structure, compressive strength, in vitro degradability in phosphate-buffered solution (PBS), bioactivity, cytocompatibility and in vitro coagulation tests were characterized and investigated. The results showed that compressive strength of the CaY/PAA composites ranged from 145 to 186 MPa, demonstrating sufficient mechanical strength for load-bearing bone substitute. After soaking in PBS for 16 weeks, the weight loss of 25CaY/PAA and 50CaY/PAA were 4.1 and 1.6 wt%, respectively, and the pH values for CaY/PAA composites increased to about 8.0 in 2 weeks and then gradually stabilized around 7.4, indicating good stability in PBS. Scanning el...