A thermochemical study of glasses and crystals along the joins silica-calcium aluminate and silica-sodium aluminate
1982
Abstract Enthalpies of solution in molten 2PbO · B 2 O 3 at 985 K are reported for series of glasses xCa 0.5 AlO 2 -(1− x ) SiO 2 ( O ≤ x ≤ 0.99) and xNaAlO 2 -(1− x ) SiO 2 (0 ≤ x ≤ 0.56). The data are compared to values for the corresponding crystalline aluminosilicates and to preliminary data for systems containing KAlO 2 and Mg 0.5 AlO 2 . The enthalpies of mixing of glasses become more exothermic with increasing basicity of the mono- or divalent oxide. The tendency toward immiscibility on the silica-rich side, indicated by the shape of the heat of mixing curve between x = 0 and x = 0.4, is pronounced in the calcium aluminate system, but not in the sodium aluminate system. The shape of the heat of mixing curve, which is roughly symmetrical about x = 0.5, can be rationalized in terms of glass structure by considering essentially random substitution of Si and Al on a continuous three dimensional tetrahedral framework, with stabilization arising from electrostatic interactions between aluminum and the nonframework cation balancing the destabilizing effects arising from perturbation of the aluminosilicate framework by the nonframework cation. These trends are consistent with the variation of physical properties of aluminosilicate melts.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
21
References
144
Citations
NaN
KQI