Preparation of Edible Films from Soybean Meal

Effect of extraction pH on mechanical properties such as tensile strength (TS) and elongation (E) and on water vapor permeability (WVP) of soybean protein isolate (SPI) edible films extracted from soybean meal was investigated. Five pHs, acidic range (pH 2.0 and pH 3.0), neutral range (pH 7.0) and alkalic range (pH 10.0 and 12.0), were used to extract SPI. TS of the film extracted at pH 7.0 was the lowest, and WVP of (SPI extracted at pH 3) film was the lowest value among the films. The WVP of films was and increased to as film thickness increased from to thickness. Three different plasticizers (glycerol, polyethylene glycol and propylene glycol) were used for (SPI extracted at pH 2) film. TS of films was 12.297 MPa and decreased to 1.356 MPa for glycerol and showed the same trend in other two plasticizers. The SPI films extracted at acidic range were shown higher mechanical properties and lower water vapor permeabilities than those of extracted at neutral and alkalic ranges. The difference of SPI film properties seemed to be attributed by 11S/7S ratio as well as protein content.