Evaluation of Hot Pressed Silicon Nitride as a Rolling Bearing Material

A series of tests has been conducted to evaluate the suitability of silicon nitride as a bearing material for rolling contact applications. The ability of silicon nitride to be lubricated by some conventional lubricants was found to be satisfactory. This was determined by wettability studies, lubricant film thickness and traction coefficient measurements on the optical EHD rig and friction coefficient measurements by the pin-on-disk method. The abrasive wear coefficient, measured on a lopping machine using 600 grit SiC abrasive, was found to be high compared to other ceramics. It was also dependent on the composition of the silicon nitride. Comparative rolling contact fatigue tests on steel and silicon nitride flat washers were conducted using steel rollers and balls. A high wear rate leading to grooving in the rolling track on silicon nitride was observed. The spalling resistance of silicon nitride was found to be higher than that of steel under the test conditions used. Surface interactions in the Si3N4...