Use of tungsten material for the ITER divertor

Abstract Since the ITER divertor design includes tungsten monoblocks in the vertical target where heat loads are maximal, the design to protect leading edges as well as technology R&D for high performance armor-heat sink joint were necessary to be implemented. In the R&D, the availability of the technology was demonstrated by high heat flux test of tungsten monoblock components. Not systematically but frequently macro-cracks appeared at the middle of monoblocks after 20 MW/m 2 loading. The initiation of such macro-cracks was considered to be due to cyclic exposure to high temperature, ∼2000 °C, where creep, recrystallization and low cycle fatigue were concerned. To understand correlation between the macro-crack appearance and mechanical properties and possible update of acceptance criteria in the material specification, an activity to characterize the tungsten monoblocks was launched.