Solar hydrogen production using Ce1−xLixO2−δ solid solutions via a thermochemical, two-step water-splitting cycle
2012
Abstract The reactivity of Ce 1− x Li x O 2− δ ( x =0.025, 0.05, 0.075 and 0.1) solid solutions during the redox and two-step water-splitting cycles has been investigated in this work. Thermogravimetric analysis (TGA), X-ray diffraction (XRD) patterns and field-emission scanning electron microscopy (FE-SEM) indicate that there are two reaction mechanisms in the O 2 -releasing step and the shift in the reaction mechanisms occurs in the O 2 -releasing step because of sintering at high temperatures, and a decrease in the concentration of lattice oxygen occurs as the O 2 -releasing step proceeds. The reaction in the O 2 -releasing step follows a second-order mechanism over a temperature range of 1000–1170 °C and a contracting-area model over a temperature range of 1170–1500 °C. According to direct gas mass spectroscopy (DGMS), ceria doped at 5 mol% Li exhibits the highest reactivity in the O 2 -releasing step during both redox cycles in air and two-step water-splitting cycles, whereas ceria doped at 2.5 mol% Li yields the highest amount of hydrogen (4.79 ml/g) in the H 2 -generation step during the two-step water-splitting cycles, which is higher than ceria doped with other metals. DGMS and electrochemical impedance spectroscopy (EIS) suggest that the average reaction rate in the H 2 -generation step is influenced by the concentration of extrinsic oxygen vacancies, and thus, the reactivity in the H 2 -generation step, to some degree, could be tuned by varying the concentration of extrinsic oxygen vacancies (Li content).
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
31
References
37
Citations
NaN
KQI