Microstructural development in reduced activation ferritic alloys irradiated to 200 dpa at 420°C
1994
Abstract Density change and microstructural development are reported for nine reduced activation ferritic steels covering the range 2.3 to 12Cr with varying additions of V and/or W for hardening and up to 6.5 Mn for austenite stability. Specimens were examined following irradiation in FFTF/MOTA at 420°C to a dose exceeding 200 dpa. Void swelling was found, but the swelling remained at 5% or below, with the worst case in an alloy of 9Cr-2Mn-1WV. The carbide structure pinning martensite lath boundaries remained in place.