THERMAL AND ELECTRON-BEAM IRRADIATION EFFECTS ON THE SURFACES OF NIOBIUM FOR RF CAVITY PRODUCTION
2001
Results of a study of thermal and electron-beam irradiation effects on the surfaces of Nb are presented. The samples were prepared by chemical etching methods used in superconducting rf cavity production. For such prepared samples, a layer of Nb2O5 covered the surface with some Nb2O interfacing the Nb metal. Some hydrocarbon species were also found on the surface. Oxidation in air at room temperature will be discussed. Heating the samples at temperatures from 100 - 300 °C caused reduction of the surface oxide. The reduction rate increased with temperature. Near 100 °C, some Nb2O5 reduced and some NbOx (x 70 h. Substantial amounts of NbOx (1 ≤ x 210 °C, Nb2O5 disappeared. Only Nb2O remained on the surface that exhibited a metallic character. In addition, more than half of the surface carbon reacted with Nb and formed metal carbide. Reaction kinetics will be discussed. Under 1-keV electron beam irradiation, surface damage occurred. Changes in the secondary electron yield (SEY) were observed and identified to be due to two causes: surface chemical changes and defect creation in the oxide. There was a slope change in the SEY-vs-dose relationship that led to two cross-section values of 4.8 × 10 -18 cm 2 and 2.3× 10 -19 cm 2 for the electron/matter interaction. The larger value primarily results from changes in surface chemistry and the smaller one from defect creation.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
1
References
7
Citations
NaN
KQI