Temperature Dependence on Dielectric Response of La0.7Ba0.3Mn0.4Ti0.6O3 Ceramic

Ceramic sample of La0.70Ba0.30Mn0.40Ti0.60O3 oxide has been prepared by the conventional solid-state reaction method. The sintered sample was characterized by using x-ray diffraction (XRD) and low frequency LCR meter. XRD result shows that the sample has a cubic structure with the existence of impurity phase. The dielectric properties of La0.70Ba0.30Mn0.40Ti0.60O3 measured from room temperature to 200°C shows that the dielectric permittivity is temperature dependence with strong dispersion at low frequencies. A circuit model based on the universal capacitor response function is also being used to represent the dielectric properties of the sample.