Interplay of cross-plane polaronic transport and resistive switching in Pt–Pr0.67Ca0.33MnO3–Pt heterostructures

The identification of the cross-plane electric transport mechanisms in different resistance states of metal–oxide sandwich structures is essential for gaining insights into the mechanisms of resistive switching (RS). Here, we present a systematic study of cross-plane electric transport properties of Pr0.67Ca0.33MnO3 (PCMO) thin films sandwiched by precious Pt metal electrodes. We observe three different transport regimes: ohmic, nonlinear and RS. The nonlinear regime is associated with colossal magneto-resistance (CMR) and colossal electro-resistance (CER) effects. In contrast to RS, the CMR and CER are volatile resistance effects which persist only during application of strong magnetic or electric fields and they are restricted to low temperatures. At low current densities, the device resistance is dominated by small polaron hopping transport of the PCMO film. At higher electric current densities near the switching threshold, the interface resistance starts to dominate and remarkably also exhibits thermally activated transport properties. Our studies also shed light onto the interplay of colossal resistance effects and RS: at low temperatures, RS can be only induced by reduction of the PCMO resistivity through CMR and CER. This clearly demonstrates the key role of the current density for controlling the amplitude of non-volatile resistive changes. Conversely, the CMR can be used as a probe for the switching induced changes in disorder and correlations. At small switching amplitudes, we observe slight changes in polaron activation energy which can be attributed to changes at the interface. If the switching amplitude exceeds 1000% and more, the CMR effect in the device can be reversibly changed. This indicates persistent changes in electronic or lattice structure of large regions within the PCMO film.