Interdiffusion in Ni-rich, Ni-Cr-Al alloys at 1100 and 1200 C. I - Diffusion paths and microstructures. II - Diffusion coefficients and predicted concentration profiles

Interdiffusion in Ni-rich Ni-Cr-Al alloys is investigated experimentally after annealing at 1100 and 1200 C using gamma/gamma, gamma/gamma+beta, gamma/gamma+gamma prime, and gamma/gamma+alpha diffusion couples. The amount and location of Kirkendall porosity suggests that Al diffuses more rapidly than Cr which diffuses more rapidly than Ni in the gamma phase of Ni-Cr-Al alloys. The location and extent of maxima and minima in the concentration profiles of the diffusion couples indicate that both cross-term diffusion coefficients are positive. Measurements are also presented of the ternary interdiffusion coefficients of the gamma phase in the Ni-Cr-Al system. It is shown that the interdiffusion coefficients can be accurately predicted by using a ternary finite-difference interdiffusion model.