Low-temperature sintering of ferroelectric Pb(Zr, Ti)O3 thick films derived from stable sol-gel solutions

Abstract We have studied sintering and densification of PbZr0.52Ti0.48O3 (PZT) films derived from diol-based sol-gel solutions. We found that densification by sintering began at below 750°C and completed at 850°C in 5 min. Initially, 0.83- μm-thick PZT single-coated films were prepared on Pt/Ti/SiO2/Si substrates from stable propylene-glycol (l,2-propanediol)-based solutions by crystallization at 700°C. The crystallized films consisted of fine perovskite grains and voids. We studied the firing temperature dependence of various properties such as microstructure, crystallinity, and ferroelectric properties for the single-coated films. Finally, 0.54- μm-thick PZT single-coated dense films were prepared by firing at 850°C for 5 min. In order to prepare thicker PZT dense films, we studied low-temperature sintering of PZT multicoated thick films. Using this approach, 1.7- μm-thick PZT dense films were prepared by firing at 850°C for 5 min.