Low Sintering of the Temperature-Stable Dielectric Ceramics Based on Barium Titanate in Reducing Atmosphere

The optimized composition and sintering process of the low sintering X7R-type temperature-stable dielectric ceramics based on Barium Titanate in reducing atmosphere have been investigated. Flux aids SiO2-B2O3-Li2O were used in the experiments. The influence of composition and the content of flux agent on the microstructures and properties of ceramics materials were systemically studied. The X7R-type dielectric ceramics materials could be sintered at low temperature of 950oC in H2/N2 atmosphere, by optimizing flux content and adjusting process parameters. The dielectric constant of ceramics was effectively improved using two-step sintering process.