Phase equilibrium of the Gd–Fe–Co system at 873 K

Abstract Phase equilibrium of the ternary Gd–Fe–Co system at 873 K was investigated by using X-ray diffraction technique, electron probe microanalysis, metallographic analysis and differential thermal analysis. The 873 K isothermal section of the phase diagram of the Gd–Fe–Co ternary system consists of 11 single-phase regions, 16 two-phase regions and 6 three-phase regions. Three pairs of corresponding compounds of Gd–Co and Gd–Fe, i.e., Gd 2 Co 17 and Gd 2 Fe 17 , GdCo 3 and GdFe 3 , GdCo 2 and GdFe 2 , form a continuous series of solid solution. The compound Gd 2 Co 7− x Fe x was found to have a broad solubility range from 0 to 31 at.% Fe. The maximum solubility of Co in Gd 6 Fe 23 is about 7 at.% Co. At 873 K, the maximum solubilities of Fe in Gd 3 Co and Gd 4 Co 3 are about 3 and 1 at.% Fe, respectively. No ternary compound was found in all ternary alloy samples.