Exchange-coupling of hard and soft magnetic sublattices and magnetic anomalies in mixed spinel NiFe0.75Cr1.25O4 nanoparticles

Abstract A set of single-crystalline nanoparticles (NPs) of nickel-chromium ferrite NiFe 0.75 Cr 1.25 O 4 with a cubic spinel structure were synthesized and investigated. The NPs size can be varied from about 5 to 50 nm by the final annealing of the precursor at different temperatures. The distribution of cations over the tetrahedral (A) and the octahedral [B] sites (Fe 0.75 Ni 0.25 ) [Ni 0.75 Cr 1.25 ] O 4 was established from the magnetic and Mossbauer measurements. In large NPs, the magnetic structure at low temperatures is close to the collinear antiferromagnetic (AFM) structure of the Neel type; and the total magnetic moment M tot of the ferrite coincides with the direction of the B-sublattice moment. Several size-dependent magnetic anomalies were revealed. Three types of magnetic ions present in the A- and B- sublattices cause the competition of AFM and FM exchange interactions resulting in the highly frustrated magnetic ordering and the occurrence of canted magnetic structure in the octahedral B-sublattice. The frustrated structure is very flexible and significantly subjected to temperature and applied field. It results in several magnetic anomalies observed, including the occurrence of magnetic compensation, abnormal behavior of ZFC and FC magnetization curves and hysteresis loops. It was shown that magnetic anomalies can be explained in terms of exchange coupling of “soft” and “hard” magnetic B- and A-sublattices. This effect in the (Fe 0.75 Ni 0.25 ) [Ni 0.75 Cr 1.25 ] O 4 NPs can be considered as an atomic-scale analog of a similar effect observed in two-phase exchange-coupled alloys developed for permanent magnets and for the perpendicular recoding media.