Non-standing spin-waves in confined micrometer-sized ferromagnetic structures under uniform excitation

A non-standing characteristic of directly imaged spin-waves in confined micrometer-sized ultrathin Permalloy ( Ni 80 Fe 20) structures is reported along with evidence of the possibility to alter the observed state by modifications to the sample geometry. Using micromagnetic simulations, the presence of the spin-wave modes excited in the Permalloy stripes along with the quasi-uniform modes was observed. The predicted spin-waves were imaged in direct space using time resolved scanning transmission x-ray microscopy, combined with a ferromagnetic resonance excitation scheme (STXM-FMR). STXM-FMR measurements revealed a non-standing characteristic of the spin-waves. Also, it was shown by micromagnetic simulations and confirmed using STXM-FMR results that the observed characteristic of the spin-waves can be influenced by the local magnetic fields in different sample geometries.A non-standing characteristic of directly imaged spin-waves in confined micrometer-sized ultrathin Permalloy ( Ni 80 Fe 20) structures is reported along with evidence of the possibility to alter the observed state by modifications to the sample geometry. Using micromagnetic simulations, the presence of the spin-wave modes excited in the Permalloy stripes along with the quasi-uniform modes was observed. The predicted spin-waves were imaged in direct space using time resolved scanning transmission x-ray microscopy, combined with a ferromagnetic resonance excitation scheme (STXM-FMR). STXM-FMR measurements revealed a non-standing characteristic of the spin-waves. Also, it was shown by micromagnetic simulations and confirmed using STXM-FMR results that the observed characteristic of the spin-waves can be influenced by the local magnetic fields in different sample geometries.