Polymerization of lactams XII. Branching of ε‐caprolactam with bislactams

Copolymers of e-caprolactam with bislactams were prepared and the crosslinking ability of individual bislactams was estimated on the basis of the copolymer solubility in m-cresol. The branching ability established on the basis of the ratio of intrinsic viscosities of the branded and linear polymer with the same Mw depends on the chemical structure of bislactams and serves simultaneously as a measure of their copolymerization ability. Further, a branched sample of poly-e-caprolactam was fractionated and a dependence of the intrinsic viscosity on Mw was obtained. This dependence, showing a deviation from the dependence for the linear poly-e-caprolactam, indicates that the degree of branching increases with the molecular weight of the fractions. Es wurden Copolymerisate von e-Caprolactam mit Bislactamen hergestellt und die Vernetzungswirksamkeit der einzelen Bislactame auf Grund der loslichkeit der Copolymerisate in m-Kresol beurteilt. Auf die Verzweigungwirksamkeit wurde aus dem Verhaltnis der Viskositatszahlen des verzwigtn und linearen Polymerisates mit gleichem Mw geschlossen. Es wurde festgestellt, das die Verzweigungswirksamkeit von der chemischen Struktur der Bislactame abhangt und das sie gleichzeitig als Mas fur die Copolymerisier-barkeit der Bislactame dienen kann. Ferner wurde eine verzwight Probe des Poly-e-caprolactams fraktioniert und die Abhangigkeit der Viskositatszahlen von Mw festgestellt. Diese Abhangigkeit, die eine Abweichung von der Abhangigkeit fur das lineare Poly-e-caprolactam aufweist, zeigt, das der Verzweigngsgrad mit dem Molekulargewicht der Fraktionen wachst.