Mechanical properties of friction welded joint between Ti–6Al–4V alloy and Al–Mg alloy (AA5052)

AbstractThe present paper describes the mechanical properties of a friction welded joint between Ti–6Al–4V alloy and Al–Mg alloy (AA5052). The Ti–6Al–4V/AA5052–H112 joint, made at a friction speed of 27.5 rev s−1, friction pressure of 30 MPa, friction time of 3.0 s, and forge pressure of 60 MPa, had 100% joint efficiency and fractured in the AA5052–H112 base metal. The Ti–6Al–4V/AA5052–H34 joint, made under the same friction welding conditions, did not achieve 100% joint efficiency and it fractured in the AA5052–H34 base metal because the AA5052–H34 base metal had softened under friction heating. The joints made at low friction speed or using short friction time showed fracture at the welded interface because a sufficient quantity of heat for welding could not be produced. However, the joints made at high friction speed or using long friction time were also fractured at the welded interface: in this instance, the welded interface also had an intermetallic compound layer consisting of Ti2Mg3Al18. The Ti–6A...