A novel method to prepare microporous and nanofibrous hydrogel scaffolds as neural tissue engineering

AbstractA new method to prepare poly (vinyl alcohol) hydrogels by nebulization method.is introduced. A blend of Poly (vinyl alcohol) (PVA), sodium gum malate (SGM) and cellulose nanofibers (CNFs) originated from Catha Edulis was prepared and tested as neural tissue substitutes. Glutaraldehyde (GLA) was used as a crosslinker. Presence of SGM and CNFs in the formulation improved the nebulization process of PVA solution as well as mechanical properties of the fabricated hydrogels. The tensile strength of neat PVA films attains 46.7 MPa, while the tensile strength was 94.23 MPa for crosslinked-PVA. The tensile strength was found to increase with the increase in the CNFs content in the PVA compared with PVA/SGM. These soft tissues were characterized by using FTIR, SEM, and DSC. Scanning electron microscopy (SEM) results showed that PVA/SGM/CNFs blends has a diameter about 50 ± 8µm. The hydrogels were tested also for antimicrobial activities against pathogenic bacteria like Candida albicans (fungus), Bacillus s...