Probing Structure-Induced Optical Behavior in a New Class of Self-Activated Luminescent 0D/1D CaWO4 Metal Oxide–CdSe Nanocrystal Composite Heterostructures

In this report, we synthesize and characterize the structural and optical properties of novel heterostructures composed of (i) semiconducting nanocrystalline CdSe quantum dots (QDs) coupled with (ii) both one- and zero-dimensional (1D and 0D) motifs of self-activated luminescent CaWO4 metal oxides. Specifically, ∼4 nm CdSe QDs have been anchored onto (i) high-aspect ratio 1D nanowires, measuring ∼230 nm in diameter and ∼3 μm in length, as well as onto (ii) crystalline 0D nanoparticles (possessing an average diameter of ∼80 nm) of CaWO4 through the mediation of 3-mercaptopropionic acid (MPA) as a connecting linker. Composite formation was confirmed by complementary electron microscopy and spectroscopy (i.e., IR and Raman) data. In terms of luminescent properties, our results show that our 1D and 0D heterostructures evince photoluminescence (PL) quenching and shortened PL lifetimes of CaWO4 as compared with unbound CaWO4. We propose that a photoinduced electron transfer process occurs from CaWO4 to CdSe QDs...