Mechanical property evaluation of an Al-2024 alloy subjected to HPT processing

An aluminum-copper alloy (Al-2024) was successfully subjected to high-pressure torsion (HPT) up to five turns at room temperature under an applied pressure of 6.0 GPa. The Al-2024 alloy is used as a fuselage structural material in the aerospace sector. Mechanical properties of the HPT-processed Al-2024 alloy were evaluated using the automated ball indentation technique. This test is based on multiple cycles of loading and unloading where a spherical indenter is used. After two and five turns of HPT, the Al-2024 alloy exhibited a UTS value of ~1014 MPa and ~1160 MPa respectively, at the edge of the samples. The microhardness was measured from edges to centers for all HPT samples. These results clearly demonstrate that processing by HPT gives a very significant increase in tensile properties and the microhardness values increase symmetrically from the centers to the edges. Following HPT, TEM examination of the five-turn HPT sample revealed the formation of high-angle grain boundaries and a large dislocation density with a reduced average grain size of ~80 nm. These results also demonstrate that high-pressure torsion is a processing tool for developing nanostructures in the Al-2024 alloy with enhanced mechanical properties.