Oxidation behaviour of an intermetallic Ti-Al-Cr-Zr bond coat on a γ-TiAl based TNB alloy with 7YSZ thermal barrier coating

AbstractIntermetallic titanium aluminide alloys are attractive light-weight materials for high temperature applications in automotive and aero engines. The development of γ-TiAl alloys over the past decades has led to their successful commercial application as low pressure turbine blades. The operating temperatures of γ-TiAl based alloys are limited by deterioration in strength and creep resistance at elevated temperatures as well as poor oxidation behaviour above 800 °C. Since improvement in oxidation behaviour of γ-TiAl based alloys without impairing their mechanical properties represents a major challenge, intermetallic protective coatings have aroused increasing interest in the last years.In this work, a 10 μm thick intermetallic Ti–46Al–36Cr–4Zr (in at.-%) coating was applied on a TNB alloy using magnetron sputtering. This layer provided excellent oxidation protection up to 1000 °C. Microstructural changes in this coating during the high temperature exposure were extensively investigated using scanni...