X‐ray reciprocal‐space mapping of strain relaxation and tilting in linearly graded InAlAs buffers
1996
The extent of relaxation and orientation of linearly graded InxAl1‐xAs (x=0.05–0.25) buffers grown on GaAs were examined using a novel x‐ray diffraction reciprocal‐space mapping technique (kmap). Samples were grown at temperatures ranging from 370 to 550 °C. The fractional relaxation of the buffers grown between 470 and 550 °C was essentially identical (77%) and symmetric in orthogonal 〈110〉 directions. These buffers are believed to be in equilibrium indicating that the incomplete relaxation is not a kinetic effect. The extent of relaxation was less than that expected for equilibrium relaxation in the absence of dislocation–dislocation interactions indicating that such interactions must be considered to accurately predict the extent of relaxation. The saturation of the relaxation as a function of temperature indicates that at the grading rate used (8% In/μm or 0.69% strain/μm), we are not working in a growth regime where the relaxation is nucleation limited. In addition, all the buffers are slightly tilte...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
43
References
66
Citations
NaN
KQI