전자세라믹 : 소결 온도에 따른 0.94(Na0.5K0.5)NbO3-0.06(Sr0.5Ca0.5)Tio3-0.1 Mno2의 압전 특성

In this study, lead-free Piezoelectric (Na0.47K0.47Sr0.03Ca0.03)(Nb0.94Ti0.06)O3-0.1 MnO2 ceramics werefabricated using mixed oxide method and the effects of various sintering temperature on the structural andelectrical properties were investigated. For the (Na0.47K0.47Sr0.03Ca0.03)(Nb0.94Ti0.06)O3-0.1 MnO2 (NKN-SCT-MnO2)ceramics sintered at temperatures of 1,025∼1,100℃. The results indicated that all specimens were perovskitesingle phase formation without any second phase. It has been shown that relative density is increased toincreasing sintering temperature. When the sintered temperature at 1,075℃, highest sintered density andmaximum value of 4.45 g/cm3. Average grain size is increased to increasing sintering temperature. Theelectromechanical coupling factor, dielectric constant, dielectric loss, d33 and curie temperature at the sinteringtemperature 1,075℃ of NKN-SCT-MnO2 specimens were 0.22, 511, 0.033, 103 and 380℃, respectively.