Hard TiCx/SiC/a-C:H nanocomposite thin films using pulsed high energy density plasma focus device

Abstract Thin films of TiC x /SiC/a-C:H were synthesized on Si substrates using a complex mix of high energy density plasmas and instability accelerated energetic ions of filling gas species, emanated from hot and dense pinched plasma column, in dense plasma focus device. The conventional hollow copper anode of Mather type plasma focus device was replaced by solid titanium anode for synthesis of TiC x /SiC/a-C:H nanocomposite thin films using CH 4 :Ar admixture of (1:9, 3:7 and 5:5) for fixed 20 focus shots as well as with different number of focus shots with fixed CH 4 :Ar admixture ratio 3:7. XRD results showed the formation of crystalline TiC x /SiC phases for thin film synthesized using different number of focus shots with CH 4 :Ar admixture ratio fixed at 3:7. SEM results showed that the synthesized thin films consist of nanoparticle agglomerates and the size of agglomerates depended on the CH 4 :Ar admixture ratio as well as on the number of focus shots. Raman analysis showed the formation of polycrystalline/amorphous Si, SiC and a-C for different CH 4 :Ar ratio as well as for different number of focus shots. The XPS analysis confirmed the formation of TiC x /SiC/a-C:H composite thin film. Nanoindentation results showed that the hardness and elastic modulus values of composite thin films increased with increasing number of focus shots. Maximum values of hardness and elastic modulus at the surface of the composite thin film were found to be about 22 and 305 GPa, respectively for 30 focus shots confirming the successful synthesis of hard composite TiC x /SiC/a-C:H coatings.