Controllable synthesis of hierarchical nickel cobalt sulfide with enhanced electrochemical activity

Abstract The composition of nickel cobalt sulfide has great influence on its electrochemical performance. Herein, the nickel cobalt sulfide with different composition and mixed phase were synthesized by one-step solvothermal method through changing the molar ratio of Ni to Co in the reaction system. The electrochemical measurements showed that the nickel cobalt sulfide with a theoretical molar ratio of Ni/Co to be 1.5:1.5 (NCS-2) demonstrates the superior pseudocapacitive performance with a high specific capacitance (6.47 F cm −2 at 10 mA cm −2 ) and a favorable Coulombic efficiency (∼99%). Whereas, when applied as the catalyst for hydrogen evolution reaction in 1 M KOH aqueous electrolyte, the nickel cobalt sulfide with a theoretical molar ratio of Ni/Co is 1:2 (NCS-1) displays better catalytic activity, and it requires a relatively lower overpotential of 282 mV to deliver the current density of 10 mA cm −2 .