High temperature thermoelectric properties of Ca3Co4O9+δ by auto-combustion synthesis and spark plasma sintering

Abstract A rapid method for the synthesis of Ca 3 Co 4 O 9+ δ powder is introduced. The procedure is a modification of the conventional citric-nitrate sol–gel method where an auto-combustion process is initiated by a controlled thermal oxidation–reduction reaction. The resulting powders inherit the advantages of a wet chemical synthesis, such as morphological and compositional homogeneity, and fine, well-defined particle sizes coming from the controlled nature of the auto-combustion. Optimized spark plasma sintering (SPS) processing conditions were determined and used to fabricate dense and highly c -axis oriented samples. The microstructure and thermoelectric transport properties were determined both parallel (||) and perpendicular (⊥) to the SPS pressure axis in order to investigate any possible anisotropy variations in the transport properties. At 800 °C, power factors of 506 μW/m K 2 (⊥) and 147 μW/m K 2 (||), thermal conductivities values of 2.53 W/m K (⊥) and 1.25 W/m K (||), and resulting figures-of-merit, ZT , of 0.21 (⊥) and 0.13 (||) were observed.