Nitrogen acceptors in bulk ZnO (0001¯) substrates and homoepitaxial ZnO films

Bulk single crystals of unintentionally doped ZnO having charge carrier concentration, ND−NA values of ∼1017 cm−3 were implanted with N+ ions at dosages of 1015 and 1016 cm−2 at 95 keV to a depth of 150 nm. The resulting p−n structure having acceptor concentrations ranging from 1017 to 1018 cm−3 was compared with nitrogen doped homoepitaxial films with ∼8×1017 cm−3 acceptors. Photoluminescence spectra acquired at 8 K showed an increase in the peak for the neutral donor-bound to acceptor-bound transition at 3.210 eV with increasing annealing temperature, thermal activation of a unique donor to acceptor transition due to nitrogen at 3.067 and 3.057 eV for implanted and epitaxial films, respectively; and an increase in the intensity of the defect-related green band at selected temperatures. Electroluminescence measurements at 300 K revealed an ultraviolet band, direct band-to-band recombination at 3.34 eV, donor-acceptor pair recombinations at 3.19 and 3.0 eV, and recombination in the green region centered a...