Homoepitaxial Growth on 4H-SiC (03-38) Face by Sublimation Close Space Technique

For preliminary step toward fabrication of MOSFET using 4H-SiC 8) 3 (03 prepared by sublimation method, epitaxial growth of device quality 4H-SiC on 4H-SiC (0001) 8.0° off substrate was carried out and investigated. Smooth and specular surface of 4H-SiC (0001) plane was obtained by optimum growth condition. And epitaxial growth on 4H-SiC 8) 3 (03 and ) 8 3 (03 substrates were carried out with optimum growth conditions of 4H-SiC (0001). Smooth and specular surface was obtained on 4H-SiC 8) 3 (03 and ) 8 3 (03 plane. Growth rate of epilayers of 4H-SiC (0001), 8) 3 (03 and ) 8 3 (03 face were same. Oxidation rate of 4H-SiC (0001), ) 1 (000 , 8) 3 (03 and ) 8 3 (03 face was investigated. The oxidation rate was different depending on the faces. It was observed that the difference of oxidation rate of 8) 3 (03 and ) 8 3 (03 is mainly due to the difference of polarity similar to the case of reported for (0001) and ) 1 (000 .