Remote atmospheric-pressure plasma activation of the surfaces of polyethylene terephthalate and polyethylene naphthalate.

The surfaces of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalate) (PEN) were treated with an atmospheric-pressure oxygen and helium plasma. Changes in the energy, adhesion, and chemical composition of the surfaces were determined by contact angle measurements, mechanical pull tests, and X-ray photoelectron spectroscopy (XPS). Surface-energy calculations revealed that after plasma treatment the polarity of PET and PEN increased 6 and 10 times, respectively. In addition, adhesive bond strengths were enhanced by up to 7 times. For PET and PEN, XPS revealed an 18−29% decrease in the area of the C 1s peak at 285 eV, which is attributable to the aromatic carbon atoms. The C 1s peak area due to ester carbon atoms increased by 11 and 24% for PET and PEN, respectively, while the C 1s peak area resulting from C−O species increased by about 5% for both polymers. These results indicate that oxygen atoms generated in the plasma rapidly oxidize the aromatic rings on the polymer chains. The Langmuir adso...