Film thickness dependence of critical current density for YBa2Cu3O7 films post-annealed at a low oxygen partial pressure

1993 
The variation of critical current density at 77 K as a function of film thickness was studied for YBa2Cu3O7 films on (100) LaAlO3 substrates. Film thicknesses were in the range 0.2–1.6μm. The films were deposited by co-evaporation and post-annealed under conditions which have previously resulted in high-quality films (750°C and an oxygen partial pressure of 29 Pa). The critical current density at 77 K exceeds 1 MA cm−2 for the thinner films, and decreases with increasing film thickness in excess of about 0.4μm. The decrease is in rough agreement with a switch fromc-axis toa-axis growth at about this critical thickness. A good anticorrelation was found between room temperature resistivity and critical current density at 77 K. The results are compared to those obtained before by post-annealing at 850°C in 1 atm of oxygen.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    20
    References
    7
    Citations
    NaN
    KQI
    []