Effects of the Transition Metal Oxides Substituted for Mg on the Electrical Conductivity of La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ -based Electrolytes

La/sub 0.8/Sr/sub 0.2/Ga/sub 0.8/Mg/sub 0.2/O/sub 3-δ/-based solid electrolytes in which Mg site was partially substituted by Fe, Co or Ni (0.05, 0.1, 0.15 at.％) were fabricated by conventional solid-state reaction and their sintered densities were above 94％ of theoretical density. X-ray diffraction analysis and microstructure observation for the sintered specimens were performed. The ac complex impedance were measured at 400。C to l000。C in air and fitted with a Solatron ZView program. The electrical conductivity of La/sub 0.8/Sr/sub 0.2/Ga/sub 0.8/Mg/sub 0.2/O/sub 3-δ/-based solid electrolytes substituted by Fe, Co or Ni was higher than that of pure La/sub 0.8/Sr/sub 0.2/Ga/sub 0.8/Mg/sub 0.2/O/sub 3-δ/. The electrical conductivity of La/sub 0.8/Sr/sub 0.2/Ga/sub 0.8/Mg/sub 0.05/Ni/sub 0.15/O/sub 3-δ/ electrolyte was 3.4×10/sup -2/ Scm/sup -1/ at 800。C and the highest value of the whole electrolytes.