Synthesis of novel sonocatalyst Er3+:YAlO3/Nb2O5 and its application for sonocatalytic degradation of methamphetamine hydrochloride

Abstract The composited sonocatalyst Er 3+ :YAlO 3 /Nb 2 O 5 was prepared by ultrasonic dispersion and high temperature calcinations method. The microstructure of Er 3+ :YAlO 3 was prepared via sol-gel method and Nb 2 O 5 was prepared by hydrothermal method. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectrometer (EDX), ultraviolet–visible (UV–vis) spectra and photoluminescence (PL) spectra, respectively. The sonocatalytic decomposition activity of composite sonocatalyst Er 3+ :YAlO 3 /Nb 2 O 5 was investigated by using ultrasound as sound source and methamphetamine hydrochloride as the target degradation product. The influences of composite sonocatalyst Er 3+ :YAlO 3 /Nb 2 O 5 with different ratios, calcination temperature, ultrasonic power, ultrasonic temperature and recycle times were investigated. The results showed that the sonocatalytic degradation rate was 82.17% after 5 h sonocatalytic decomposition under the condition of ultrasonic power of 700 W, frequency of 45 kHz and surrounding temperature of 30 °C. The sonocatalytic degradation ability of composite sonocatalyst for methamphetamine hydrochloride in aqueous solution was still good after recycled five times. The hydroxyl radicals ( OH) and holes (h + ) are identified and hydroxyl radicals ( OH) plays a major role during the oxidation process. The experimental results show that sonocatalytic is a new idea for the harmless treatment of amphetamine-type stimulants.