The Influence of Hot Rolling Technological Parameters on Microstructure of Low Temperature Grain-Oriented Silicon Steel

The process of hot rolling Fe-3.15% Si steel is simulated by Gleeble-3500 thermal mechanical simulator, the influence of finishing temperature, coiling temperature and cooling rates after rolling on microstructure of Fe-3.15% Si steel are mainly researched, and the influence of hot rolled microstructure on Goss texture, secondary recrystallization and magnetic property are analysed. The results show that the nonuniform microstructures of hot rolled strip play an important role in developing the perfect secondary recrystallization. Fe-3.15% Si steel is rough rolled at 1110°C, finished rolled at 880°C, subsequently cooled to 550°C for coiling at rate of 10°C/s, then air cooled to room temperature. The above mentioned process could produce hot-rolled microstructure which are benefit to formation of Goss texture and the development of perfect secondary recrystallization.