Cu2ZnSnS4 thin film solar cells from electroplated precursors: Novel low-cost perspective
2009
Abstract Thin-film solar cells based on Cu 2 ZnSnS 4 (CZTS) absorbers were fabricated successfully by solid-state reaction in H 2 S atmosphere of electrodeposited Cu–Zn–Sn precursors. These ternary alloys were deposited in one step from a cyanide-free alkaline electrolyte containing Cu(II), Zn(II) and Sn(IV) metal salts on Mo-coated glass substrates. The solar cell was completed by a chemical bath-deposited CdS buffer layer and a sputtered i-ZnO/ZnO:Al bilayer. The best solar cell performance was obtained with Cu-poor samples. A total area (0.5 cm 2 ) efficiency of 3.4% is achieved ( V oc = 563 mV, j sc = 14.8 mA/cm 2 , FF = 41%) with a maximum external quantum efficiency (EQE) of 80%. The estimated band-gap energy from the external quantum efficiency (EQE) measurements is about 1.54 eV. Electron backscatter-diffraction maps of cross-section samples revealed CZTS grain sizes of up to 10 µm. Elemental distribution maps of the CZTS absorber show Zn-rich precipitates, probably ZnS, and a Zn-poor region, presumably Cu 2 SnS 3 , close to the interface Mo/CZTS.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
7
References
378
Citations
NaN
KQI