Crosslinking network of bio‐based bis‐functional epoxides derived from trans‐limonene oxide
2019
The thiol‐ene reaction between trans‐limonene oxide (trans‐LO) and ethane‐1,2‐dithiol in the presence of triethylborane affords a bio‐based bis‐functional epoxide (bis‐trans‐LO). The crosslinking reaction of bis‐trans‐LO with branched polyethyleneimine (BPEI; Mₙ = 600; BPEI₆₀₀) at a feed ratio of bis‐trans‐LO/BPEI₆₀₀ = 57/43 (wt/wt) yields the corresponding network polymer with Td₁₀ (10% thermal decomposition temperature) of 304.7 °C in 98% yield. In contrast, negligible amounts of network polymer are obtained by the reaction of bis‐LO (bis‐functional epoxide derived from cis and trans‐LO) and BPEI₆₀₀ regardless of the feed ratio. The mechanical strengths as measured by direct tensile tests of the network polymers derived from bis‐trans‐LO and BPEI₆₀₀,₁₈₀₀ (Mₙ = 600 and 1800) were approximately 16 and 11 times higher than that of bis‐LO and BPEI₁₈₀₀, respectively. The tensile shear strengths of the metal‐to‐metal adhesive bonds induced by bis‐trans‐LO and BPEI₆₀₀,₁₈₀₀ were 9.5 and 14.1 MPa, respectively. DMA revealed that the storage modulus of the network polymer derived from bis‐trans‐LO and BPEI₁₈₀₀ in the rubber region was higher than that of the material prepared from bis‐LO and BPEI₁₈₀₀, indicating higher crosslink density of the bis‐trans‐LO/BPEI₁₈₀₀ system. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 2466–2473
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
19
References
2
Citations
NaN
KQI