Temperature Dependence of the Magnetic Properties of a Co-Rich Amorphous Alloy after Field, Stress, and Stress-Field Annealing

After annealing treatments under stress, field, or both of them, we measure the temperature dependence of the induced anisotropy, the initial susceptibility, and the coercivity in order to get information about the mechanism producing the induced anisotropy and the dominant magnetization process in an amorphous Co-rich alloy. It is concluded that the field induced anisotropy is due to short-range atomic pair ordering, while the stress induced anisotropy is an effect caused by the atomic bond rearrangement which in turn generates an anisotropy via magnetic interaction. The domain pattern after each annealing treatment is shown, indicating the direction of induced anisotropy and the kind of magnetization process. Es wird die Temperaturabhangigkeit der induzierten Anisotropie, der Anfangssuszeptibilitat und der Koerzitivfeldstarke nach Temperbehandlungen unter Einflus von Zugspannung und/oder Magnetfeld bestimmt, um Informationen uber den Mechanismus der Ausbildung einer Anisotropie und den vorherrschenden Magnetisierungsprozes in einer amorphen Co-reichen Legierung zu erhalten. Die induzierte Anisotropie wahrend einer Magnetfeldtemperung bildet sich durch lokale Umorientierung von Atompaaren. Dagegen wird nach einer Zugspannungstemperung durch eine Umordnung von Atombindungen die Anisotropie uber magnetische Wechselwirkung verursacht. An Hand der Domanenstruktur nach der jeweiligen Anlasbehandlung erkennt man die induzierte leichte Richtung und die Art des Magnetisierungsprozesses.