Photopolymerizable phosphate acrylates as comonomers in dental adhesives with or without triclosan monomer units

Abstract Phosphate diacrylates (CO-DAP, TMP-DAP) based on castor oil or trimethylolpropane were synthesized and evaluated in dental adhesive formulations in comparison with 3-acryloyloxy-2-hydroxypropyl methacrylate phosphate (AMP-P). In an attempt to promote antibacterial activity, another photopolymerizable monomer (TCS-UMA) containing 5-chloro-2-(2,4-dichlorophenoxy)phenol moiety (triclosan) was prepared and incorporated in adhesive resins. Each of these monomers had a molecular structure confirmed by spectral methods. The photopolymerization rates for monomers (0.063–0.088 s − 1 ) were lower than those determined in the monomer combinations (0.116–0.158 s − 1 ) incorporating phosphate diacrylate (11 wt.%), BisGMA (33 wt.%), TEGDMA (10 wt.%), UDMA (10 wt.%) and HEMA (15 wt.%), the degree of conversion varying between 63.4 and 74.5%. The formed copolymers showed high values for water sorption (18.65–57.02 μg/mm 3 ) and water solubility (3.51–13.38 μg/mm 3 ), and the contact angle was dependent on the presence of CO-DAP (θ F1 : 66.67°), TMP-DAP (θ F2 : 55.05°) or AMP-P (θ F3 : 52.90°) in the photocrosslinked specimens compared to the sample without phosphate monomer (θ F4 : 82.14°). The scanning electron microscopy image of the dentin–resin composite interface after applying our F1 formulation (pH: 4.1) and its light-curing for 20 s supports the evidence of the formation of the hybrid layer with the tooth structure created by self-etching approach, with no gaps or cracks in the adhesive. A comparative analysis of the adhesion achieved with commercial adhesive systems (Single Bond Universal, C-Bond) rather indicates similarities than differences between them. The addition of triclosan methacrylate (1 wt.%) into the formulation inhibited the bacterial growth of the Streptococcus mutans and Escherichia coli in the direct contact area due to the covalently linked antibacterial monomer.