Friction Stir Lap Welding 0.8-mm-Thick 2024 Aluminum Alloy with the Assistance of Stationary Shoulder
2019
In this work, 0.8-mm-thick 2024 aluminum alloy was friction stir lap welded with the assistance of a stationary shoulder system. The joint surface formation, microstructure and mechanical properties of the welded joints were studied. The results showed that sound joints without defect could be obtained at a wide parameter range because stationary shoulder increased the material flow during welding. The stationary shoulder decreased the joint roughness from 125.5 to 58.9 µm. A thickness reduction of 4% was achieved at a welding speed of 200 mm/min. The joint fabricated by the stationary shoulder system had superior lap shear properties compared to the joint fabricated using the conventional tool. A high failure load of 7440 N was achieved at welding speed of 200 mm/min. The joint presented tensile fracture mode and the fracture morphology showed typical ductile fracture.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
21
References
3
Citations
NaN
KQI